The influence of organic plasticizers based on Mg2+ lignin-sulphonates (LS), naphthalene derivatives (NF) and melamine-formaldehyde polyconden-sates (PC) on the parameters of solidified FBC-P (fluidised bed combustion product) was tested. Water-reducing effectiveness of the additives tested in-creases in the following order: NF, PC, LS. All additives cause a marked in-crease in compressive strength of solidified specimens prepared from suspension of constant workability and reduced amount of mixing water. The compressive strength increases predominantly with the volume weight of specimens and the time of hardening. The conductivity of leachate of modi-fied specimens has tendency to decrease with the dose of additives and to increase with the time of leaching up to about 100 days of leaching and af-terwards it decreases. UV spectral analysis showed that the content of LS and PC molecules in the leachate after 24 hours of leaching is very low, near to the detection limits of the method used.
Badano wpływ organicznych plastyfikatorów opartych na sulfonianach ligninowych (SL), pochodnych naftalenu (PN) i polikondensatach melaminowo-formaldehydowych (PMF) na parametry zestalonego produktu spalania złoża fluidalnego. Skuteczność w ograniczaniu niszczącego wpływu wody w badanych dodatkach zwiększała się w następującym porządku: PN, PMF, SL. Wszystkie dodatki znacznie zwiększały wytrzymałość na ściskanie zestalonych próbek otrzymanych z zawiesiny o stałej podatności na obróbkę i obniżonej zawartości dodanej wody. Wytrzymałość na ściskanie zwiększa się najczęściej z ciężarem objętościowym próbek i czasem twardnienia. Przewodność właściwa odcieku po ługowaniu zmodyfikowanych próbek zmniejsza się z dawką dodatków, a zwiększa się z czasem ługowania do około 100 dni, po czym spada. Analiza w zakresie UV wykazała, że zawartość cząsteczek SL i PMF w odcieku po 24 godzinach ługowania jest bardzo mała, bliska granicy wykrywania stosowanej metody.
Słowa kluczowe
Czasopismo
Rocznik
Tom
Strony
53--64
Opis fizyczny
Bibliogr. 14 poz., rys., tab.
Twórcy
autor
- Tomáš Bata University, Faculty of Technology, Masarykovo Náměstí 275,762 72 Zlín, Czech Republic.
autor
- VUT-Faculty of Civil Engineering, Veveti 95, 662 37 Brno, Czech Republic.
autor
- Tomáš Bata University, Faculty of Technology, Masarykovo Náměstí 275,762 72 Zlín, Czech Republic.
Bibliografia
- [1] SEBOK T., VоNDRUŚКА M., BEDNARIK V., KULISEK K., Leaching of pollutants from solidified flying ash with high content of calcium sulfate and calcium oxide, Environment Protection Engineering, 2000, Vol. 27, No. 1, pp. 49-58.
- [2] OGAWA K., ROY D.M., СЗАЗS hydration, ettringite formation, and its expansion mechanism: III Effect of Cal, Nail and NaCI, conclusions, Cern. Con, Res., 1982, Vol. 12, No. 2, pp. 247-256.
- [3] SEBOK T., SIMONIK J., KULISEK K., The compressive strength of samples containing fly ash with high content of calcium sulfate and calcium oxide, Cem. Con. Res., 2001, Vol. 31, No. 7, pp. 1101-1107.
- [4] GUERRERO A., Gist S., MACINS A., LUXAN A.M., Effect of the starting fly ash on the microstructure and mechanical properties of fly ash - belite cement mortars, Cern. Con. Res., 2000, Vol. 30, No. 4, pp. 553-559.
- [5] KAMON M., KATSUMI T., Utilization of coal fly ash from fluidized bed combustion systems, Geoenvironment, 2000, ASCE, pp. 1765-1779.
- [6] МА W., BROWN P.W., Hydrothermal reactions of fly ash with Сa(0Н)2 and Ca504 2120, Cern. Con. Res., 1977, Vol. 27, No. 8, pp. 1237-1248.
- [7] CLARK B.A., BROWN P.W., The formation of calcium sulfo-aluminate hydrate compounds. Part II, Cern. Con. Res., 2000, Vol. 30, No. 2, pp. 233-240.
- [8] POON C.S., Kou S.C., LAM L., LIN Z.S., Activation of fly ash/cement system using calcium sulfate anhydrite (Ca504), Cern. Con. Res., 2001, Vol. 31, No. 2, pp. 873-881.
- [9] MA W., LIU Ch., BROWN P.W., KOMARENI S., Pore structures of fly ash activated by Сa(OН)2 and Ca504 21120, Cern. Con. Res., 1995, Vol. 25, No. 2, pp. 417-425.
- [10] LI D., CHEN Y., SHEN J., SU J., WU X., The influence of alkalinity on activation and microstructure of fly ash, Cern. Con. Res., 2000, Vol. 30, No. 6, pp. 881-886.
- [11] СНROМY S., MAKI I., Determination of the quantitative phase composition of alite and belite in Portland cement clinker by microphotometry, Cern. Con. Res, 1982, Vol. 12, No. 4, 511-516.
- [12] АNDЁL J., Mathematical Statistics (in Czech), 1975, State Publishing Company SNTL, Prague.
- [13] SEBOK T., MUSIL A., study of rhelogical properties of consistent binding pastes, Cement and Concrete Research, 1986, Vol. 16, No. 1, 1-6.
- [14] SEBOK Т., VONDRUSKА M., Interaction of anhydrite and melamine formaldehyde polycondensates in aqueous suspensions, Cement and Concrete Research, 2000, Vol. 30, No. 6, 993-1003.
Typ dokumentu
Bibliografia
Identyfikator YADDA
bwmeta1.element.baztech-article-BPG5-0010-0015
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.